生物兼容三类医疗ISO 10993 TPE, 生物兼容三类医疗TPE

 

生物兼容三类医疗ISO 10993 TPE, 生物兼容三类医疗TPE, ISO 10993, 生物兼容性

 

Versaflex™ HC 3810-70N

热塑性弹性体

 

普立万公司

 

Technical Data

 

产品说明

Versaflex™ HC 3810-70N is a general purpose, unfilled TPE compound used for healthcare applications

总览

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet

搜索 UL 黄卡 •  普立万公司

• Versaflex™

供货地区 • 北美洲

用途 • 医疗/护理用品

机构评级 • ISO 10993 Part 4 2 • ISO 10993 Part 5

RoHS 合规性 • RoHS 合规

外观 • 半透明

形式 • 粒子

加工方法 • 注射成型

物理性能 额定值(英制) 额定值(公制) 测试方法

密度 / 比重 0.880 0.878g/cm³ ASTM D792

弹性体 额定值(英制) 额定值(公制) 测试方法

拉伸应力 4, 5 (300%应变, 73°F (23°C)) 684psi 4.72MPa ASTM D412

抗张强度 4, 5 (断裂, 73°F (23°C)) 1000psi 6.90MPa ASTM D412

伸长率 4, 5 (断裂, 73°F (23°C)) 570% 570% ASTM D412

压缩永久变形 ASTM D395B

73°F (23°C), 22 hr 28% 28%

158°F (70°C), 22 hr 43% 43%

硬度 额定值(英制) 额定值(公制) 测试方法

肖氏硬度 (邵氏 A, 10 秒) 72 72 ASTM D2240

充模分析 额定值(英制) 额定值(公制) 测试方法

表观粘度 (392°F (200°C), 11200 sec^-1) 7.60Pa•s 7.60Pa•s ASTM D3835

注射 额定值(英制) 额定值(公制)

建议的最大回制料比例 20% 20%

料筒后部温度 330 到 370°F 166 到 188°C

料筒中部温度 350 到 380°F 177 到 193°C

料筒前部温度 370 到 440°F 188 到 227°C

射嘴温度 360 到 420°F 182 到 216°C

加工（熔体）温度 380 到 440°F 193 到 227°C

模具温度 60 到 100°F 16 到 38°C

注射说明

Color concentrates with polypropylene (PP), ethylene vinyl acetate (EVA), or low density polyethylene (PE) carriers are most suitable for coloring Versaflex™ HC 3810-70N. Improved color dispersion can be achieved by using higher melt flow concentrates (with a melt flow from 25 - 40 g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Concentrates based on PVC should not be used. The final determination of color

concentrate suitability should be determined by customer trials.

Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).

Regrind levels up to 20% can be used with Versaflex™ HC 3810-70N with minimal property losses, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should be as low as possible. The final determination of regrind effectiveness should be determined by the customer.

 

Versaflex™ HC 3810-70N has excellent melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.

Drying is not Required

 

 

 

生物兼容三类医疗ISO 10993热塑性弹性体,生物兼容三类医疗ISO 10993 TPE Versaflex™ HC 3810-70N是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，COA原料出厂报告,REACH报告,SVHC报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123   13549213581 肖生    QQ：15397858   微信：13549213581